Bakin Karfe Round Bars suna zuwa da maki iri-iri waɗanda ake amfani da su a masana'antu daban-daban.Ana amfani da sanduna zagaye na bakin ƙarfe saboda ƙarfinsu da juriya ga lalata.Chromium yana cikin duk bakin karfe.Bakin Karfe Round Bars sun zo cikin diamita daga 4mm zuwa 500mm.Tsawon sandunan ya bambanta daga mita 1 zuwa 6.Hakanan akwai girma da tsayi na al'ada.Mu ne kuma masu samar da Bakin Karfe 304 Round Bars, Bakin Karfe 304L Round Bars, Bakin Karfe 316 Round Bars, da dai sauransu.
| Tsawon Karfe Bakin Karfe | 2 zuwa 6 mita ko 8 zuwa 20 ƙafa |
| Bakin Karfe Rod Chamfering | Akwai a cikin 30, 45 & 60 digiri ta hanyar cikakken atomatik biyu-karshen chamfering inji |
| Gwajin Ultrasonic na ASTM A276 Threaded Rod | Dangane da ASTM A-388, EN 10308 (aji na 1 zuwa 4), API 6A/ISO an gwada 100% ta hanyar Digital Ultrasonic Flaw Detector, 10423: 2003-PSL 3, MIL-STD 2154, SEP 1920: 1984 |
| Bakin Karfe Round Bar Girman Hakuri | h11 |
| Haƙuri na Tsawon Sanyi Round SS | Hannun jari a cikin yanke na musamman zuwa sandar tsayi cikin haƙuri - 0/+ 10mm (-0 + 0.5 inch) |
| Farfajiya ta gama sanyaya sandar ss zagaye | Zane sanyi ko yanayin goge bel |
| Maganin Zafin Zafi Na Round Bar | Annealed da Magani Annealed |
| Daraja | Tsawaitawa | Yawan yawa | Ƙarfin Ƙarfin Ƙarfi | Ƙarfin Haɓaka (0.2% Kashe) | Matsayin narkewa |
| Farashin SS202 | 40% | 8.0 g/cm 3 | 515 MPa | 275 MPa | 1454C (2650F) |
| Farashin SS303 | 50% | 55% | Psi - 85,000 | Psi - 45,000 | Rb 180 |
| Farashin SS304 | 40% | 8.0 g/cm 3 | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 1400C (2550F) |
| Saukewa: SS304L | 40% | 8.0 g/cm 3 | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 1400C (2550F) |
| Farashin SS316 | 35% | 8.0 g/cm 3 | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 1454C (2650F) |
| Saukewa: SS316L | 40% | 8.0 g/cm 3 | 485 Min | 170 Min. | 1400C (2550F) |
| Babban darajar ASTM | Carbon | Manganese | Siliki | Sulfur | Phosphorous | Chromium | Nickel | Molybdenum | Sauran |
| 304 | 0.08 max | 2.00 max | 0.75 max | 0.030 max | 0.045 max | 18.0-20.0 | 8.0 11.0 | - | - |
| 316 | 0.08 max | 2.00 max | 0.75 max | 0.030 max | 0.045 max | 16.0-18.0 | 10.0 14.0 | 2.0 3.0 | - |
| 317l | 0.035 max | 2.00 max | 0.75 max | 0.030 max | 0.045 max | 18.0-20.0 | 11.0 14.0 | 3.0 4.0 | - |
| 310 S | 0.08 max | 2.00 max | 1.5 max | 0.030 max | 0.045 max | 24.0-26.0 | 19.0 22.0 | 3.0 4.0 | - |
| 347 H | 0.04 0.10 | 2.00 max | 0.75 max | 0.030 max | 0.045 max | 17.0-19.0 | 9.0 13.0 | - | 10C (Cb+Ta) <1.10% |
| 321 | 0.08 | 2.00 max | 0.75 max | 0.030 max | 0.045 max | 17.0-20.0 | 9.0 12.0 | - | 5C 0.70% |
| Diamita | Jadawalin Nauyi | Dia | Jadawalin Nauyi |
| (mm) | kowace mita (kg) | (cikin) | kowace mita (kg) |
| 3 mm | 0.06 | 1/8" | 0.06 |
| 4mm ku | 0.10 | 3/16" | 0.14 |
| 5mm ku | 0.16 | 1/4" | 0.25 |
| 6mm ku | 0.22 | 5/16" | 0.39 |
| 7mm ku | 0.30 | 3/8" | 0.56 |
| 8mm ku | 0.40 | 7/16" | 0.77 |
| 10 mm | 0.62 | 1/2" | 1.00 |
| 12mm ku | 0.89 | 9/16" | 1.22 |
| 14mm ku | 1.22 | 5/8" | 1.56 |
| 15mm ku | 1.40 | 11/16" | 1.89 |
| 16mm ku | 1.59 | 3/4" | 2.25 |
| 18mm ku | 2.01 | 7/8" | 3.07 |
| 20mm ku | 2.48 | 1" | 4.03 |
| 22mm ku | 3.00 | ||
| 24mm ku | 3.57 | ||
| 25mm ku | 3.88 |